Planar array infrared (PA-IR) spectroscopy was used to study polyphenylene sulfide (PPS) at room temperature during the application of a sinusoidal elastic deformation. All of the intensity in the dynamic spectra was contained within the in-phase spectrum, which was expected since the measurements were carried out at room temperature, far below the glass transition temperature. The contributions of chain orientation, sample thinning, and stress-induced band shifts were separated in the dynamic spectra. It was found that the effects of chain orientation and sample thinning canceled each other out. Stress-induced band shifts far below the spectral resolution, on the order of 0.01 cm<sup>−1</sup>, were quantified and used to calculate the stress optical coefficients and mode Gruneisen parameters for PPS.
You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an OSA member, or as an authorized user of your institution.
Contact your librarian or system administrator
Login to access OSA Member Subscription